75μm Thermal Film Industrial Rough Surfaces Label Material — S9J201

Construction

The three functional layers of this item. Selecting on face stock alone is where most specification errors begin — the adhesive and liner decide how it behaves on your press.

Product features

• Hot melt adhesive system — good heat resistance for demanding environments
• Thermal film face — combines print convenience with durability

FAQ

S9J201 (75μm Thermal Film): does the Hot Melt adhesive on 62g White Glassine give enough grab at the rough, dusty or low-energy parts edge, and does the liner change the answer?

75μm Thermal Film is specified for the industrial rough surfaces field, which does not mean every substrate in it. Thermal film puts the heat-sensitive coating on a film base, so it also resists water. Not recommended for PVC surfaces; small diameters, irregular or squeezable bottles.

Is there a storage limit on S9J201 (75μm Thermal Film, Hot Melt) once it sits on a 62g White Glassine liner, and does the liner shift it?

The minimum application temperature is 10 °C and the service range after labelling is -15–65 °C. Below the minimum the adhesive cannot wet out, and edges lift within hours on a curved wall. Both figures are measured at 23±2 °C / 50±5 % RH, so confirm them with a trial roll on your line.

Do the peel figures for S9J201 (75μm Thermal Film, Hot Melt) change with the 62g White Glassine liner, and is that a 20 min or 24 h value?

Initial tack is ≥20 N by the ball method and 90° peel is ≥12 N/25 mm after 20 min. Both are measured to FINAT FTM 9 and FTM 2 at 23±2 °C / 50±5 % RH. Peel grows with dwell, so compare the same hold time against your own pull test.

How much S9J201 (75μm Thermal Film, Hot Melt) on a 62g White Glassine liner do we have to order, and how long does it take, and can it be pooled with other codes?

Minimum order quantity is 500 ㎡ and lead time is 15 days after artwork and roll-format approval. A trial roll for press approval can be arranged before the production run starts. Shipment is ex-works Guangzhou, and it can be consolidated with other codes on the same order.

How does S9J201 (75μm Thermal Film) compare with S9RG31 on rough, dusty or low-energy parts, and can we get both as samples?

S9J201 runs Hot Melt adhesive on 62g White Glassine Liner, while S9RG31 runs Removable on 62g White Glassine Liner. The difference is the adhesive chemistry, which decides edge lift and high-speed behaviour more than the face does. Compare the two technical tables above, then test both on the same substrate.